(Ron Thornton) wrote in message ...
Bruce,

The "ordinary" people are the ones that can best justify epoxy because
the quantity they typically us is small compared to the production user.

To answer your question about why to use epoxy instead of poly is, that
it makes a better repair.

Regards, Ron

I don't recieve e-mail at this address because of spam. E-mail me
at crtsrATmsnDOTcom.

But that is really not even much of a factor anymore. To build a 12
foot skiff with flotation and proper materials, it is going to cost
you $250.00 on materials and hardware alone (assuming exterior plywood
hull), and just for ha ha's, say $25 for a set of plans. If you use
poly instead of epoxy, you might save $25 to $30 bucks max on the
whole build and more times than not, I have seen first time builders
end up using 2-3 times more poly than the plan would call for. The
learning curve for mixing poly is treacherous, (bring a good scale and
a calculator too) especially to the home builder that may be building
outdoors, or in a non conditioned barn, tent, etc.

Let me take a minute for anyone who is not clear about mixing the two
products.
With polyester, you must first calculate your catalyst ratio. So many
ounces of resin, to so many drops of catalyst. This mixture is not
only very delicate, but it changes depending on ambient temp,
humidity, how fast you want things to cure and the required
differences in the catalyst mixtures is very minute, and are based on
the starting formula plus the users best guess or experience of how to
alter that formula to suit the conditions at the time. Any very slight
miscalculation in the mix or even how many clouds will pass over
during the application can cause total havoc resulting in a slimy hot
slop all over your boat that is extremely difficult to remove (think
half hardened plastic mixed with cold roofing tar), that is to hard to
scrape, and to soft to sand, or a fast kick which catches you with
only half of your glass saturated, or just gobs up thicker and thicker
as you try to catch up and save something. In both cases the only
solution is a lot of elbow grease and lot's of wasted time and sand
paper, scrapers, and then a re-application.
With Epoxy, the cure rate is also dependant on the temp and humidity
of the work area, but not nearly as fast or as radical. Mixing is done
with calibrated pumps, something like one pump of resin to one pump of
hardener. If you want a faster cure, substitute a "fast" hardener, if
slower is your style or a bigger area to do in warmer weather, use a
slower hardener, no calculators, no precision scales, no guesswork at
all. If your pumps are working properly, and you don't get lazy
mixing, even mistakes will harden nicely to be ground or sanded off.

One extreme case (admittedly the most extreme I am aware of) was a
couple of years ago when I came in very late by e-mail on a build of
"Diablo", a 15 foot Bolger type skiff. The plan calls for 2 1/2
gallons of resin. This guy had a terrible summer of heat and cold,
never really got the mixtures down in his one build. He spent
literally dozens of hours scraping and sanding and just throwing out
resin that either kicked to fast, or not at all. He ended up using 11
gallons of poly on the build at a total cost of over $200 for resin
alone. Not to mention lost thickeners, thinners, brushes, sand paper,
scrapers, time, time, time, time, time... I will stop now, but he has
since built another boat, but this time he used epoxy, no problems.
Now I don't expect any first timer to build Diablo with 2 1/2 gallons
of resin, but certainly 3-3 1/2 should be the max.

One final comment. I do not know what the original poster should do, I
have no experience there, I don't do restores ;-) I also do realize
that poly has it's place in composite shops where big lay-up is done
or for molded parts, but somehow this thread seemed to get hijacked to
my area so I thought I would chime in here. So this has been my
advice, take if for what you paid.
Scotty from SmallBoats.com

Thread Tools	Search this Thread
Show Printable Version	Search this Thread: Advanced Search
Display Modes
Switch to Linear Mode Switch to Hybrid Mode Threaded Mode

Similar Threads
Thread	Thread Starter	Forum	Replies	Last Post
Epoxy or Poly for poly repairs?	Lloyd Sumpter	Boat Building	14	January 4th 04 12:29 AM
epoxy does so pass water	William R. Watt	Boat Building	14	November 11th 03 12:52 PM
Epoxy sales	carlp	Boat Building	11	October 11th 03 08:57 PM
Polyester epoxy	carlp	Boat Building	8	October 2nd 03 09:07 PM
polyester - epoxy bonding	Walt	Boat Building	19	July 27th 03 06:37 PM

Menu

About Us